Epoxy curing agent Knowledge Application of 2-sulfobenzoic anhydride_Kain Industrial Additive

Application of 2-sulfobenzoic anhydride_Kain Industrial Additive

广告位

Background and overview[1]

2-Sulfobenzoic anhydride is an acid anhydride derivative and can be used in the pharmaceutical and chemical fields.

Preparation[1]

The preparation of 2-sulfobenzoic anhydride is as follows: under N2 protection, add 9.0g saccharin solid and 13mL concentrated sulfuric acid (concentration 98%) into a 50mL three-necked flask, stir and react at 140°C for 2 hours, and then cool to room temperature. , a large amount of solid precipitated from the reaction mixture, filtered, and the solid obtained by filtration was washed with ice water and dried to obtain 7.3g of 2-sulfobenzoic anhydride white solid, with a yield of 81%. The obtained 2-sulfobenzoic anhydride was subjected to nuclear magnetic spectrum analysis, and the results were as follows: 1HNMR (500MHz, CDCl3) δ8.77 (d, J=7.3Hz, 1H), 8.05 (d, J=7.3Hz, 1H) , 7.76 (t, J=2.2Hz, 1H), 7.53 (t, J=8.5Hz, 1H).

Apply[2-3]

Application examples of 2-sulfobenzoic anhydride are as follows:

1) Preparation of flame-retardant, light-resistant water-based polyurethane coating: In a 500ml four-necked flask equipped with a stirring paddle, a thermometer, and a condenser tube, combine 0.6g of the catalyst in step (1), 80g of polytetrahydrofuran ether glycol and isophora Mix 40g of ketone diisocyanate and react at 70℃ for 1 hour. Add 0.2g of 2-sulfobenzoic anhydride and 0.05g of carboxylated graphene sheet from step (3). The reaction time is 2h and the reaction temperature is 80℃ to obtain polyurethane prepolymer. Prepolymer A; add 1.2g of aminobenzenesulfonic acid and 20g of acetone to prepolymer A, react at 75°C for 2 hours, add 1g of 2,4,6-trihydroxybenzoic acid and 1.2g of the light-stabilizing agent in step (2) , the reaction temperature is 85°C, the reaction time is 0.5h, add 12g of triethylamine for neutralization reaction for 30 minutes, add 110g of water for stirring and emulsification, and obtain a flame-retardant and light-resistant water-based polyurethane coating. The prepared polyurethane is environmentally friendly, low-priced, and widely used in On the surface of walls, furniture, and metal appliances, it can be used as an adhesive for plastics, glass, paper, and textiles.

2) Prepare a carbon nanotube graphene modified water-based polyurethane coating and adhesive by mixing polytetrahydrofuran ether glycol and isophorone diisocyanate in the presence of a dibutyltin dilaurate catalyst. , react at 60~80℃, add 2-sulfobenzoic anhydride, carboxylated carbon nanotubes and graphene sheets, the reaction time is 2h, the reaction temperature is 90℃, and polyurethane prepolymer A is obtained; to prepolymer A Add chain extender and acetone, react at 65~75℃, add D-panthenol and 2,4,6-trihydroxybenzoic acid, reaction temperature 75~85℃, reaction time 0.5~2h, add triethylamine and Neutralize benzamide for 30 to 50 minutes, add water for emulsification, and obtain carbon nanotube graphene-modified water-based polyurethane coating and adhesive. The prepared polyurethane is environmentally friendly, low-priced, and widely used in walls, furniture, and metal appliances. Surface, as an adhesive for plastics, glass, paper, and textiles.

Main reference materials

[1] CN201811467727.5 Synthesis process of rhodamine sulfonate compound

[2] CN201810881113.5 Preparation method of flame-retardant, light-resistant water-based polyurethane coating for preparing furniture or metal utensils

[3] CN201510699527.2 Method for preparing carbon nanotube graphene modified water-based polyurethane coating and adhesive

广告位
This article is from the Internet, does not represent the position of Epoxy curing agent, reproduced please specify the source.https://www.dmp-30.vip/archives/16828

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: info@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Follow Weibo
Back to top
Home
Phone
Products
Search