Product Introduction
Takenate D-110N is a curing agent that is an aliphatic polyisocyanate synthesized from xylylene diisocyanate (XDI) and dissolved in ethyl acetate.
Features
Good weather resistance, yellowing resistance and adhesion;
The curability is better than that of TDI aromatic polyisocyanate;
Used in conjunction with polyols, castor oil and other hydroxyl-containing resins, it is mainly used in coatings, adhesives, and sealing materials.
Status Properties
|
Appearance |
Light Yellow transparent liquid |
|
ChromaG |
1 Max. |
|
Solid content% |
75.0 ±1.0 |
|
Viscosity 25°C, mPa·s |
500 ±400 |
|
NCO content% |
11.5 ±0.5 |
|
FreeXDI monomer% |
0.5 Max. |
Coating film physical properties*
|
Main agent |
Takelac U-27(polyester polyol) |
|
Mixing ratio, NCO/OH molar ratio |
1.0 |
|
Acupressure is dry,h |
2.4 |
|
Activity, h |
8 |
|
Adhesion |
100 /100 |
|
Erickson value, mm |
8 |
|
Bending resistance,mm |
2 |
|
Impact resistance |
|
|
DuPont method, inch x g x cm |
1 /2 x 1000 x 50 |
|
Pencil hardness |
H |
*The data provided here are measured during normal use only and do not represent the specifications of this product.
Application Scope
Can be used as coating components for woodworking, furniture, interior decoration, vehicles, paper, plastic coatings, outdoor protective coatings, adhesives, sealants, ink adhesives, etc.
Notes
Please refer to the MSDS for health and safety related information about this product.